12/31/2011 These high-quality brass rods are manufactured as per various national and international standards like :
Free Cutting Brass Rods
IS 319/89 - Grade I
IS 319/89 - Grade II
IS 319/89 - Grade III
BS 2874 - CZ 121 Pb3
UNS C36000
BS 2874 - CZ 131
CW 614 N EN 12164 : 1998
Forging Brass Rods
BS 218
IS - 6912/2005 FLB
Modified Forging Brass Rods as per IS - 8737
CW 617 N EN 12164 : 1998
CDA 377
High Tensile Brass Rods
IS 320/80
HT-1 is suitable for soldering.
HT-2 is suitable for machining.
BS 2874 - CZ 114
BS 2874 - CZ 115
Naval Brass Rods
IS 291/89 - Grade I
IS 291/89 - Grade II
CDA 464 and CDA 385
Lead Free Brass
70:30 Lead Free Brass and
65:35 Lead Free Brass Rods.
Table 2 of British Standard Specification for Brass Rods
Name
CZ-112
Naval Brass Rods(291/89) Grade I
CZ-113
Naval Brass Rods(291/89) Grade II
CZ-108
Lead free Riveting Brass Rods & Wires IS 4413/81
CZ-109
Lead free Riveting Brass Rods & Wires IS 4170/67
AS - 2738.2
AS - 486
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Copper
61
64
59
62
62
65
59
62
59
62
Tin
1
1.5
0.5
1.0
-
-
-
-
0.80
1.50
Lead
-
0.2
0.5
1.0
-
0.30
-
0.30
1.0
2.50
Iron
-
0.1
-
0.10
-
0.10
-
0.10
-
-
Aluminium
-
-
-
-
-
-
-
-
-
-
Manganese
-
-
-
-
-
-
-
-
-
-
Nickel
-
-
-
-
-
-
-
-
-
-
Arsenic
-
-
-
-
-
-
-
-
0.02
0.25
Total Impurities
-
0.20
-
0.20
-
0.60
-
0.30
-
-
Zinc
Balance
Balance
Balance
Balance
Balance
Table 4 of Brass Rods and Sections - BS - 2874 (BS 249/63)
Name
CZ 114
Brass Rods
CZ 115
High Tensile
Brass Rods
CZ 121
Free Cutting
Brass Rods
CZ 122
(BS - 218)
Free Cutting
Brass Rods
CS 124
Free Cutting Brass Rods
IS 319 cor II
CZ 130
Leaded Brass For Section
CZ 131
(DTD - 627)
Free Cutting Brass with Improved Ductility
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Copper
56
59
56
60
56
60
56.50
60
60
63
56
58
61
63
Lead
0.50
1.50
0.5
1.50
2.0
3.50
0.60
2.0
2.5
3.7
2.50
3.50
1.5
2.5
Iron
0.50
1.20
0.5
1.20
-
-
-
0.30
-
0.35
-
-
-
-
Aluminium
-
1.50
-
0.20
-
-
-
-
-
-
-
0.40
-
-
Manganise
0.30
2.0
0.30
2.00
-
-
-
-
-
-
-
-
-
-
Tin (SN)
0.20
1.0
0.60
1.10
-
-
-
-
-
-
-
-
-
-
Zinc
-
Bal
-
Bal
-
Bal
-
Bal
-
Bal
-
Bal
-
Bal
Nickel
-
-
-
-
-
-
-
-
-
-
-
-
-
-
Silicon
-
-
-
-
-
-
-
-
-
-
-
-
-
-
Total Impurities
-
0.50
-
0.50
-
0.75
-
0.70
-
0.50
-
0.75
-
0.50
Name
Free Cutting and Forging
Brass Rods
DIN EN 17660 MS - 58
Free Cutting and Forging
Brass Rods
DIN EN 12164
DIN 17660
2.0402
Free Cutting
Forging Brass
CW614N
CW617N
CW608N
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Copper
57
59
57
59
57
59
57
59
60
61
57
59
Lead
2.50
3.50
1.50
2.50
2.5
3.5
1.60
2.50
1.6
2.5
1.50
2.50
Tin
-
0.40
-
0.30
-
0.30
-
0.30
-
0.20
-
0.30
Iron
-
0.50
-
0.40
-
0.30
-
0.30
-
0.20
-
0.40
Aluminium
-
0.10
-
0.10
-
0.05
-
0.05
-
0.05
-
0.10
Nickel
-
0.50
-
0.40
-
0.30
-
0.30
-
0.30
-
0.40
Silicon
-
-
-
-
-
-
-
-
-
-
-
-
Maganise
-
-
-
-
-
-
-
-
-
-
-
0.20
Zinc
Balance
Balance
Balance
Balance
Balance
Balance
Total Impurities
-
0.20
-
0.20
-
0.20
-
0.20
-
0.20
-
0.20
Name
BS - 218
Modified Forging
Brass
IS 6912/85 FLB
Forging Brass
(with low Mn)
High Tensile Brass Rods
As IS 320/80
Riveting Brass Wires (Leaded)
IS 2704/83
HT - 1
HT - 2
Min
Max
Min
Max
Min
Max
Min
Max
Min
Max
Copper
56.50
60.0
56.50
60.0
56
60
56
61
62
65
Lead
1.0
1.50
0.60
1.20
0.20
1.50
0.50
1.50
0.75
1.50
Tin
-
-
-
-
0.20
1.00
-
1.00
-
-
Iron
-
0.30
-
0.30
0.20
1.25
0.20
1.50
-
0.10
Aluminium
-
-
-
-
-
0.20
0.30
2.0
-
-
Manganise
-
0.50
-
0.20
0.25
2.0
0.50
2.0
-
-
Nickel
-
-
-
-
-
-
-
-
-
-
Silicon
-
-
-
-
-
-
-
-
-
-
Zinc
Balance
Balance
Balance
Balance
Balance
Total Impurities
-
0.50
-
0.25
-
0.50
-
0.50
-
0.50
Name
JIS C 3601
(H 3250)
JIS C 3604
(H 3250)
JIS C 3771
(H 3250)
Min
Max
Min
Max
Min
Max
Copper
59.00
63.00
57.00
61.00
57.00
61.00
Tin
-
0.20
-
0.20
-
0.30
Lead
1.80
3.50
1.80
3.50
0.50
2.50
Iron
-
0.30
-
0.35
-
0.35
Aluminium
-
-
-
-
-
-
Manganese
-
-
-
-
-
-
Nickel
-
-
-
-
-
-
Arsenic
-
-
-
-
-
-
Zinc
Balance
Balance
Balance
Total Impurities
-
0.50
-
0.50
-
0.50
Physical Properties
Specification
Size
(MM)
Tensile Strength (Kg / mm2 )
Min
% of Elongation 5.65
Min
0.2% Proof Stress
Hardness
HV
IZOD
Impact Value
(Kg/FM)
HT-1 IS 320/80
-
49
12
-
-
-
HT-2 IS 320/80
-
53
12
-
-
-
DIN EN 17660
MS 58
(Forging)
-
37
20
-
-
-
BS 218
Modified
Forging Brass
-
40
18
-
-
2.2
DIN EN 17660
MS 58
(Free Cutting)
-
43
15
-
-
-
Riveting Brass Wire (Leaded)
IS 2704/83
¼ Hard (HA)
½ Hard (HB)
Hard (HD)
Extra Hard (HE)
325 Mpa
400 Mpa
500 Mpa
695 Mpa
30
20
15
5
-
110 to 130
131 to 150
151 to 175
176 to 215
-
DIN EN 12164 CW 614N
-
43
10
-
-
-
DIN EN 12164 CW 617N
-
43
10
-
-
-
DIN EN 12164 CW 608N
-
40
25
-
-
-
C 3601 JIS
Annealed
½ Hard
Hard
294 Mpa
343 Mpa
451 Mpa
25
25
25
-
-
-
C 3604 JIS
-
333 Mpa
20
-
-
-
C-3771 JIS
-
314 Mpa
15
-
-
-
CZ-112
Naval Brass Gr-1
Upto 12.50
12.50 to 50
50 to 100
40
38.50
35
18
18
18
-
-
-
CZ-113
Naval Brass Gr-2
All Size
40
15
-
-
-
CZ-109
Lead Free
-
34
25
-
-
-
CZ-108
Lead Free
Annealed
Half Hard
Hard
33
47 to 63
63 to 79
35
35
35
-
-
-
CZ-114
Hard
47
55
18
12
24.5
29.5
-
-
CZ-115
-
47
20
19.50
-
-
CZ-121
Annealed 6 to 25
Annealed 25 to 50
Annealed 50 above
Half Hard 6 to 12
Half Hard 12 to 25
Half Hard 25 to 50
Half Hard 50 above
Hard 6 to 12
Hard 12 to 25
345 Mpa
315 Mpa
285 Mpa
405 Mpa
395 Mpa
355 Mpa
325 Mpa
550 Mpa
490 Mpa
12
17
22
4
6
12
17
-
4
-
-
-
CZ-122
-
310 Mpa
20
-
-
-
CZ-124
6 to 12
12 to 25
25 to 50
50 above
41
40
36
33
4
6
12
17
-
-
-
CZ-130
-
37
25
-
-
-
CZ-131
-
37
22
-
-
-
We HTE (Hitech Extrusion LLP) are a leading manufacturer and exporter of Brass Extrusion Rods, having experience of more than three decades in Brass industry. We manufacture Brass Rods, Brass Wires, Bronze Rods, Brass Casting, Brass Pipes Tubes, Brass Hollow Rods, Brass Ingots Billets, Special Coppe…
Phosphorus Bronze Ingots and Billets
Leaded Bronze Ingots and Billets
Aluminium Bronze Ingots and Billets
Brass Tubes For Agriculture Equipments
Brass Tubes For Sanitary Fittings & Accessories
Admiralty Brass Tubes For Evaporators & Coolers
Arsenic Brass Tubes For Sugar Industries
Bras Tubes For General Engineering Purpose
Brass Tubes For Furniture and lighting fixtures
Brass Wire Nickel silver wise for ball pen Tips